Technical Properties
These properties are typical but do not constitute specifications.
Item | AT6070A | AT6070B |
Type | Main agent | Hardener |
Appearance | Light yellow transparent liquid | Light yellow transparent liquid |
Solid Content(%) | 70±2 | 70±2 |
Viscosity (mPa.s20℃) | 6000±3500 | 17±5 |
Solvent | Alcohol,Ethyl acetate | Ethyl acetate |
Specific gravity | 0.93-0.97 | 0.93-0.97 |
Mix Proportion | 6 | 1 |
Shelf life | 360days | 360days |
Typical Features:
l High bonding strength.
l Suitable for middle and high-speed dry laminating machine.
l The packaging films laminated by AG6070A/B offer high bonding and peeling strength, specially suitable for products which need high-strength.
Recommended Operating Conditions
¨ Application Method Direct gravure
¨ Application Cylinder 100-200 line (65-80 line per cm)
¨ Application solids 20-35% (Recommend 30%)
¨ Pot Life Static 8 hours approximately
¨ Dynamic 24 hours approximately
¨ Dry Coating Weight 1.5-3.0 gsm depending on structure
¨ Drying Section Temperature 55-65℃ 65-75℃ 75-85℃(three section)
¨ Laminating Temperature 50-80℃
¨ Cure Time 12 hours (40-50℃)
¨ Cleaning Solvent Ethanol
Mix Ratio By Weight
Working Concentration | AT6070A | AT6070B | Alcohol(kgs) | Viscosity(Zahn cup#3/25℃)(s) |
35 | 6 | 1 | 7.0 | 38.5 |
30 | 6 | 1 | 9.3 | 25.2 |
25 | 6 | 1 | 12.6 | 17.9 |
20 | 6 | 1 | 17.5 | 14.2 |
Solvent is isopropyl, modified methanol, ethanol, purification shall be up to 95%. Ethanol is the recommended solvent.
Package
Pack in steel drum normally.
Main agent is 18kg/drum. Hardener is 3kg/drum.
Safety & Storage
Store in cool, dry, well-ventilated area away from heat and ignition sources . Keep container tightly closed.
Refer to MSDS for more safety information
Precautions
1. The LDPE and CPP films must be corona-treated with a surface tension greater than 38 mN/m. The PA film must be double-corona treated as an intermediate layer. The surface tension must not be less than 52 mN/m; the surface tension of the PET film must not be Less than 52 mN/m.
2. The temperature and humidity of the environment have a great influence on the time for storing the configured adhesive. It is recommended to arrange the adhesive in small quantities for a few times in high temperature and high humidity weather to avoid waste.
3. During the laminating processing, care must be taken to check and control the viscosity.
4. Residual adhesive: The remaining adhesive cannot be used in principle. If the amount of residual liquid is excessive, it shall be sealed and stored in cool place after dilution, which could be used as diluent for operation in next day, and a small amount shall be little by little added to the newly prepared adhesive solution. It cannot be used any more, if it appears cloudy, translucent or thickened.
5. The concentration and additives in the film have an influence on the bonding strength of the laminated film and must be selected before use.
6. Do not mix this product with other adhesives. If necessary, please consult our technical department.
7. Pay attention to fire prevention and static elimination.
Important notice
These documents we provided are made on the basis of our recent knowledge and experience, all these terms we mentioned are only suitable in normal condition and could be used as references. Please test and affirm before formal production or contact with our technician to some especial structures of films and stuffs packed, we do not take on any legal duty for these documents.