EB4160A/EB4160B ethyl acetate solvent base polyurethane adhesive
(specializing for Aluminum Foil, VMPET,VMOPP,VMCPP boiling resistant packaging)
Description
EB4160A/B is an ethyl acetate solvent base two-component polyurethane functional adhesive with excellent anti-medium, anti-auxiliaries performance , specializing for Aluminum Foil and VMPET,VMOPP,VMCPP 100℃ boiling resistant packaging ,widely used in laminating of various treated film like PET, NY, AL, PE, CPP,VMPET,VMOPP,VMCPP , etc .
Technical Properties
These properties are typical but do not constitute specifications.
Item | EB4160A (OH component) | EB4160B (NCO component) |
Type | Main agent | Hardener |
Ingredient | Polyester polyol agent | Isocyanate-terminated Polymer |
Appearance | Light yellow transparent liquid | Light yellow transparent liquid |
Solid Content(%) | 60±2 | 75±2 |
Viscosity (mPa.s) | 3000±1000(25℃) | 2500±1250(20℃)) |
Solvent | Ethyl acetate | Ethyl acetate |
Mix Proportion | 20 | 4 |
Shelf life | 360days | 360days |
Typical Features:
l EB4160A/B is a functional adhesive with very soft colloid
l Specializing for Aluminum foil laminating with good peeling strength and high transparency, resist to be boiled at 100℃ less than 40 minutes.
l With excellent anti-medium, anti-auxiliaries performance like reducing the influence of smooth agent.
l High initial and final bonding strength, good flow property, good coating property to the film, the laminated film have good resistance for film-aging, freezing etc
Recommended Operating Conditions
¨ Application Method Direct gravure
¨ Application Cylinder any types of smooth roller or anilox roller
¨ Application solids 20-40% (Recommend 30%)
¨ Pot Life Static 8 hours approximately
¨ Dynamic 24 hours approximately
¨ Dry Coating Weight 3.0-4.0 gsm depending on structure
¨ Drying Section Temperature 50-60℃ 60-70℃ 70-80℃(three section)
¨ Laminating Temperature 50-80℃
¨ Cure Time 48~96 hours (45-55℃)
¨ Cleaning Solvent Ethyl Acetate
Mix Ratio By Weight
Working concentration % | EB4160A KGS | EB4160B KGS | Ethyl Acetate KGS |
35 | 20 | 4 | 18.8 |
30 | 20 | 4 | 26 |
25 | 20 | 4 | 36 |
20 | 20 | 4 | 50.8 |
Solvent is ethyl acetate, acetone, MEK, the water content should be less than 0.03%, the alcohol content should be less than 0.02%, Ethyl acetate is recommended.
Precautions
1. The LDPE and CPP films must be corona-treated with a surface tension greater than 38 mN/m. The PA film must be double-corona treated as an intermediate layer. The surface tension must not be less than 52 mN/m; the surface tension of the PET film must not be Less than 52 mN/m.
2. The temperature and humidity of the environment have a great influence on the time for storing the configured adhesive. It is recommended to arrange the adhesive in small quantities for a few times in high temperature and high humidity weather to avoid waste.
3. During the laminating processing, care must be taken to check and control the viscosity.
4. Residual adhesive: The remaining adhesive cannot be used in principle. If the amount of residual liquid is excessive, it shall be sealed and stored in cool place after dilution, which could be used as diluent for operation in next day, and a small amount shall be little by little added to the newly prepared adhesive solution. It cannot be used any more, if it appears cloudy, translucent or thickened.
5. The concentration and additives in the film have an influence on the bonding strength of the laminated film and must be selected before use.
6. Do not mix this product with other adhesives. If necessary, please consult our technical department.
7. Pay attention to fire prevention and static elimination.
Package
Pack in steel drum normally.
Main agent is 20kg/drum. Hardener is 4kg/drum.