EB4260A/EB4260B is a high-strength, anti-aging functional two-component aromatic polyurethane adhesive. Suitable for laminating of metal/polymer printed film for can packaging, and the finished product has the characteristics of high strength, resistance to forging, corrosion resistance, etc. It can withstand 0~180° cold bending without delamination.
These properties are typical but do not constitute specifications.
Item | EB4260A (OH component) | EB4260B (NCO component) |
Type | Main agent | Hardener |
Ingredient | Polyester polyol agent | Isocyanate-terminated Polymer |
Appearance | Light yellow transparent liquid | Light yellow transparent liquid |
Solid Content(%) | 60±2 | 75±2 |
Viscosity (mPa.s) | 4000±1000(25℃) | 2500±1250(20℃) |
Solvent | Ethyl acetate | Ethyl acetate |
Mix Proportion | 5 | 1 |
Shelf life | 360days | 360days |
Recommended Operating Conditions
¨ Application Method Direct gravure
¨ Application Cylinder 60-200 line
¨ Application solids 20-40% (Recommend 30%)
¨ Pot Life Static 8 hours approximately
¨ Dynamic 12 hours approximately
¨ Dry Coating Weight 4.0-5.0 gsm
¨ Drying Section Temperature 50-60℃ 60-70℃ 70-80℃(three section)
¨ Laminating Temperature 50-80℃
¨ Cure Time Over 48 hours (45-55℃)
¨ Cleaning Solvent Ethyl Acetate
Mix Ratio By Weight
Solid content(%) | Mix Ratio | Operating Mix Ratio In Drums Weight | |||
EB4260A | EB4260B | EB4260A | EB4260B | Ethyl Acetate(kgs) | |
35 | 5 | 1 | 20 | 4 | 18.8 |
30 | 5 | 1 | 20 | 4 | 26 |
25 | 5 | 1 | 20 | 4 | 36 |
20 | 5 | 1 | 20 | 4 | 50.8 |
Solvent is ethyl acetate, acetone, MEK, the water content should be less than 0.03%, the alcohol content should be less than 0.02%, Ethyl acetate is recommended.
Humidity over than 60% , the mix ratio should be over than EB4260A:EB4260B=4:1.2
Package
Pack in steel drum normally.
Main agent is 20kg/drum. Hardener is 4kg/drum.
Safety & Storage
Store in cool, dry, well-ventilated area away from heat and ignition sources . Keep container tightly closed.
Refer to MSDS for more safety information
Important notice
These documents we provided are made on the basis of our recent knowledge and experience, all these terms we mentioned are only suitable in normal condition and could be used as references. Please test and affirm before formal production or contact with our technician to some especial structures of films and stuffs packed, we do not take on any legal duty for these documents.